X-8380 Hot Spray Polyurea Coating
X-8380 Solvent-Free 2K Hot Spray Polyurea Coating
Product Info
X-8380 is a fast-curing, solvent-free aromatic polyurea elastomer coating engineered for critical waterproofing and corrosion protection. Compliant with Chinese National Standard GB/T23446-2009 Type II, it forms a seamless, flexible barrier on primed steel, concrete, and other substrates. Designed exclusively for 1:1 ratio dual-component spray equipment, it achieves rapid film formation (surface dry: 60 sec at 24°C), drastically reducing project downtime in demanding environments like water tanks, granulation towers, and underground structures.
Key Features
✅ Ultra-Fast Cure & High Productivity
- Gel time: >20 sec | Surface dry: 60 sec (24°C, 50% RH)
- Full cure: 90% in 24 hours – accelerates project timelines
✅ Exceptional Mechanical Performance
- Tensile strength: 20 MPa | Elongation: 510%
- Tear strength: 65 KN/m | Hardness: Shore 89A
- Low-temperature flexibility: -40°C
✅ Superior Adhesion & Water Resistance
- Adhesion (primed concrete): 2.5 MPa (substrate failure)
- Adhesion (primed steel): 10.2 MPa (adhesive failure)
- Water absorption: <2%
✅ Eco-Compliant Formulation
- Solids content: >98% | Zero VOC
- Conforms to GB/T23446-2009 Type II standards
The X-8380 2K hot spray polyurea coating is ideal for:
• Water Containment: Water tanks, reservoirs, swimming pools
• Structural Waterproofing: Roofs, basements, tunnels
• Industrial Corrosion Protection: Granulation towers, chemical processing facilities
• Infrastructure: Bridges, pipelines, marine structures
Technical Parameters
| Property | Value |
|---|---|
| Volume Mixing Ratio | 1:1 |
| Gel Time (24°C, 50% RH) | >20 sec |
| Tensile Strength | 20 MPa |
| Elongation at Break | 510% |
| Tear Strength | 65 KN/m |
| Hardness | Shore 89A |
| Water Absorption | <2% |
| Low-Temperature Flexibility | -40°C |
| Adhesion (Primed Concrete) | 2.5 MPa |
| Adhesion (Primed Steel) | 10.2 MPa |
Application
1. Surface Preparation
- Apply only on pre-treated, primed substrates.
- Seal joints/gaps with compatible sealants; pre-treat corners/seams with waterproofing tape.
2. Environmental Conditions
- Do not apply when:
- Ambient temperature <4°C or >38°C
- Rain expected within 30 min or humidity >90%
3. Spray Parameters
- Equipment: 1:1 ratio dual-component airless spray rig
- Dry Film Thickness (DFT):
- Light wear: 800–1000μm
- Moderate wear: 1000–1500μm
- Severe wear: 1500–3000+μm
- Recoat window: <5 min between passes (at 24°C)
4. Quality Control
- Inspect for voids/pinholes; repair defects within 48 hours.
- Use X-7109 repair material for patching (feather edges for seamless integration).
5. Topcoat Recommendation
- For UV stability or aesthetic needs, apply a UV-resistant topcoat (contact ISOPOLYOL for options).